29 août 2017
The development of refractories has three main drivers: to maintain and improve the quality of the glass; the economic requirements of the glass furnace to make the kiln longer operating cycle and the use of pure oxygen combustion system after the impact and impact. The current changes in the electronics industry and the computer industry can be interpreted as months or weeks, and when it comes to the development and application of refractory materials in the glass industry, it can easily be interpreted as five or ten... [Lire la suite]
25 août 2017
The main problems faced by Glass Industry Refractory Materials is the development of low temperature melting. Arsenic-free material melting process, the whole oxygen combustion technology and the development of electric melting technology, refractory material to make more stringent requirements. Recent years, the life of glass melting furnace has been greatly improved, the production of flat glass float production line up to 10 years, ordinary glass melting furnace life of 5 to 7 years, special glass melting furnace life of... [Lire la suite]
22 août 2017
China's glass kiln refractory material development, will continue to focus on the life of glass melting furnace, glass product quality and cost, energy consumption and environmental protection and other aspects, that is, glass kiln refractory materials are facing the main problem is low temperature melting development of. With the glass melting furnace oxygen-rich combustion, oxygen burning, arsenic-free material melting process and electric welding technology to promote the use of refractory materials, especially cast... [Lire la suite]
18 août 2017
Modern glass production technology compared with the traditional process has been a qualitative leap, towards a higher efficiency, lower energy consumption, better product quality in the direction of continuous development. Kiln as the core of glass production equipment, its technical level is also progressing, widely used to improve the combustion strength, strengthen the heat transfer effect, reduce heat loss, reduce the product and environmental pollution and other new technologies. China's glass industry has developed rapidly,... [Lire la suite]
16 août 2017
The magnesia brick are fused magnesia as main raw material, after a reasonable size distribution, high pressure forming, high-temperature sintering. The product has strong resistance to slag corrosion ability and high temperature dimensional stability. Mainly used in the regenerator, the upper part of glass furnace. The regular magnesia bricks are made from dense dead burned magnesia that makes the bricks in good refractoriness, corrosion-resistance, and widely used in checker chamber of glass tank,... [Lire la suite]
15 août 2017
Adopts high quality silica and advanced technology, our silica bricks enjoy the advantages of high purity, long service life, good thermal conductivity, high refractoriness under load, and good creep resistance. In addition, it has accurate size tolerance, pure color and luster appearance. Because of the bad thermal shock resistance of silica brick, it is mainly used in the continuous operating furnace. Supporting the use of other high quality refractories, our silica brick can extent the service life of float glass furnace... [Lire la suite]
14 août 2017
Zircon Brick is made by the zircon ore as raw material, adding a small amount of plastic clay, mixing, compacting and calcined into clumps. The lump is then crushed and added a small amount of plastic clay or other organic binders and mixed, shaped, and burned. Calcination and firing temperature should not exceed 1600 degrees, generally can be done by 1400 hours under a long time insulation to burn. Zircon Brick from China Zhengzhou Shixing Refractory Co., Ltd. is for alkali-free glass, soda lime glass, lead glass,... [Lire la suite]
11 août 2017
Fused Cast AZS-41# Block - The best Fused Cast AZS-41# Block from China Zhengzhou Shixing Refractory.
Fused Cast AZS-41# Block with the highest ZrO₂ content produced by Shixing. This type of AZS has been widely used in the most exposed parts of glass melting furnace.Fused Cast AZS-41# Block have passed the ISO international certified, are made of high pure material, fired at high temperature by advanced technology, with the advantages of high strength, high compression resistance, good thermal shock resistance, good performance in high temperature, good thermal conductivity, good erosion resistance and so on. Widely be used... [Lire la suite]
10 août 2017
Fused Cast AZS-36# Block - The best Fused Cast AZS-36# Block from China Zhengzhou Shixing Refractory.
Fused Cast AZS-36# Block can provide improved service over AZS-33, which is a type of AZS fused cast refractory produced by Shixing having 36% ZrO₂ content.Fused Cast AZS-36# Block have passed the ISO international certified, are made of high pure material, fired at high temperature by advanced technology, with the advantages of high strength, high compression resistance, good thermal shock resistance, good performance in high temperature, good thermal conductivity, good erosion resistance and so on. Widely be used for... [Lire la suite]
09 août 2017
Fused Cast AZS-33# Block - The best Fused Cast AZS-33# Block from China Zhengzhou Shixing Refractory.
Fused Cast AZS-33# Block is the most commonly used type of AZS fused cast refractory produced by Shixing having 33% ZrO2 content. Fused cast AZS 33# block has dense micro structure which ensures its great resistance in glass liquid, thus you don’t have to worry about the solidification and other problems. It is widely applied to glass furnace for superstructure, working pool side wall, paving blocks, feeder channels, tank bottoms, C-shaped block and doghouse crown, etc. Advantages: 1. Compact microstructure 2. Good erosion... [Lire la suite]